| 牌號 : | 900p | 加工級別 : | 注塑級 |
| 特性級別 : | 增強級,耐磨,高強度,高流動,高抗沖,高剛性 | 用途級別 : | 填充級,纖維,薄壁制品 |
| 品牌 : | 美國陶氏杜邦 | 廠家(產地) : | 美國杜邦 |
| 銷售方式 : | 品牌經銷 | 類型 : | 標準料 |
產品參數
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.42 | ||
| 模收縮 | 2.2-2.4 | ||||
| 吸水量 | 50相對濕度 | ASTM D-570 | 0.22 | ||
| 吸水量 | 浸漬平衡點 | ASTM D-570 | 0.90 | ||
| 吸水量 | 24小時浸漬 | ASTM D-570 | 0.25 | ||
| 機械性能 | 洛氏硬度M | ASTM D-785 | 94 | ||
| 撓曲系數 | 23 | ||||
| ASTM D-790 | 3220 | MPa | |||
| 撓曲系數 | 100 | ||||
| ASTM D-790 | 1030 | MPa | |||
| 洛氏硬度R | ASTM D-785 | 120 | |||
| 破裂點拉伸變形量 | 23 | ||||
| ASTM D-638 | 25 | ||||
| IZOD沖擊強度 | 23 | ||||
| ASTM D-256 | 71 | j/m | |||
| 抗拉伸沖擊強度 | 長試片23 | ||||
| ASTM D-1822 | 250 | kj/m2 | |||
| 撓曲系數 | 70 | ||||
| ASTM D-790 | 1720 | MPa | |||
| IZOD沖擊強度 | 缺口-40 | ||||
| ASTM D-256 | 55 | j/m | |||
| 拉伸強度 | 70 | ||||
| ASTM D-638 | 48 | MPa | |||
| 撓曲疲勞忍耐限度 | 50RH,23,106周期 | ASTM D-671 | 32 | MPa | |
| 破裂點拉伸變形量 | -55 | ||||
| ASTM D-638 | 10 | ||||
| 壓縮應力 | 23,10變形 | ASTM D-695 | 121 | MPa | |
| 破裂點拉伸變形量 | 70 | ||||
| ASTM D-638 | 180 | ||||
| 破裂點拉伸變形量 | 100 | ||||
| ASTM D-638 | >260 | ||||
| 撓曲系數 | -55 | ||||
| ASTM D-790 | 4730 | MPa | |||
| 拉伸強度 | 23 | ||||
| ASTM D-638 | 69 | MPa | |||
| 彈性系數 | 23 | ||||
| ASTM D-638 | 3640 | MPa | |||
| 抗剪強度 | 23 | ||||
| ASTM D-732 | 66 | MPa | |||
| 撓曲系數 | 122 | ||||
| ASTM D-790 | 755 | MPa | |||
| 破裂點拉伸變形量 | 122 | ||||
| ASTM D-638 | >260 | ||||
| 撓曲變形強度 | 23 | ||||
| ASTM D-790 | 97 | MPa | |||
| 拉伸強度 | 122 | ||||
| ASTM D-638 | 26 | MPa | |||
| IZOD沖擊強度 | 無缺口23 | ||||
| ASTM D-256 | 1620 | j/m | |||
| 拉伸強度 | 100 | ||||
| ASTM D-638 | 36 | MPa | |||
| 負載變形量 | 140kg/cm2,50 | ||||
| ASTM D-621 | 0.5 | ||||
| 壓縮應力 | 23,1變形 | ASTM D-695 | 35 | MPa | |
| 拉伸強度 | -55 | ||||
| ASTM D-638 | 101 | MPa | |||
| 電氣性能 | 介電強度 | 瞬間Short time(2.3mm) | ASTM D-149 | 19.7 | kv/mm |
| 容積電阻率 | 23,0.2含水量 | ASTM D-257 | 1×1015 | Ω.cm | |
| 抗電弧 | 3.1mm | ASTM D-495 | 220 | sec | |
| 介電常數 | 50RH,23,102106Hz | ASTM D-150 | 3.7 | Ω.cm | |
| 介電因數 | 50RH,23,106Hz | ASTM D-150 | 0.005 | ||
| 熱性能 | 線性熱膨脹系數 | 2960 | |||
| ASTM D-696 | 12.2 | 10-5m/m | |||
| 自燃性 | UL 94 | HB | |||
| 熱傳導系數 | 0.37 | W/mk | |||
| 線性熱膨脹系數 | 60104 | ||||
| ASTM D-696 | 13.7 | 10-5m/m | |||
| 線性熱膨脹系數 | 104160 | ||||
| ASTM D-696 | 14.9 | 10-5m/m | |||
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 136 | ||
| 熱畸變溫度 | 0.5MPa | ASTM D-648 | 172 | ||
| 線性熱膨脹系數 | -4029 | ||||
| ASTM D-696 | 10.4 | 10-5m/m | |||
| 熔點 | |||||
| ASTM D-2133 | 175 | ||||